PVC給水管是以衛生級聚氯乙烯樹脂為主要原料，產于北京。添加定量的穩定劑、潤滑劑、填充劑、增色劑等，經塑料擠出機擠出成型和注塑機注塑成型，通過冷卻、固化、定型、檢驗、包裝等工序生產出的一種給水用管材。
 |
有需求，找我們 400-1883-191 |
在線交流 |
 |
|
公稱外徑 dn (mm) | 公稱壁厚（mm） | ||||||
| 0.63 | 0.8 | 1.0 | 1.25 | 1.6 | 2.0 | 2.5 | |
| 20 | — | — | — | — | — | 2.0 | 2.3 |
| 25 | — | — | — | — | 2.0 | 2.3 | 2.8 |
| 32 | — | — | — | 2.0 | 2.4 | 2.9 | 3.6 |
| 40 | — | — | 2.0 | 2.4 | 3.0 | 3.7 | 4.5 |
| 50 | — | 2.0 | 2.4 | 3.0 | 3.7 | 4.6 | 5.6 |
| 63 | 2.0 | 2.5 | 3.0 | 3.8 | 4.7 | 5.8 | 7.1 |
| 75 | 2.3 | 2.9 | 3.6 | 4.5 | 5.6 | 6.9 | 8.4 |
| 90 | 2.8 | 3.5 | 4.3 | 5.4 | 6.7 | 8.2 | 10.1 |
| 110 | 2.7 | 3.4 | 4.2 | 5.3 | 6.6 | 8.1 | 10.0 |
| 125 | 3.1 | 3.9 | 4.8 | 6.0 | 7.4 | 9.2 | 11.4 |
| 140 | 3.5 | 4.3 | 5.4 | 6.7 | 8.3 | 10.3 | 12.7 |
| 160 | 4.0 | 4.9 | 6.2 | 7.7 | 9.5 | 11.8 | 14.6 |
| 180 | 4.4 | 5.5 | 6.9 | 8.6 | 10.7 | 13.3 | 16.4 |
| 200 | 4.9 | 6.2 | 7.7 | 9.6 | 11.9 | 14.7 | 18.2 |
| 225 | 5.5 | 6.9 | 8.6 | 10.8 | 13.4 | 16.6 | — |
| 250 | 6.2 | 7.7 | 9.6 | 11.9 | 14.8 | 18.4 | — |
| 280 | 6.9 | 8.6 | 10.7 | 13.4 | 16.6 | 20.6 | — |
| 315 | 7.7 | 9.7 | 12.1 | 15.0 | 18.7 | 23.2 | — |
| 355 | 8.7 | 10.9 | 13.6 | 16.9 | 21.1 | 26.1 | — |
| 400 | 9.8 | 12.3 | 15.3 | 19.1 | 23.7 | 29.4 | — |
| 450 | 11.0 | 13.8 | 17.2 | 21.5 | 26.7 | 33.1 | — |
| 500 | 12.3 | 15.3 | 19.1 | 23.9 | 29.7 | 36.8 | — |
| 560 | 13.7 | 17.2 | 21.4 | 26.7 | — | — | — |
| 630 | 15.4 | 19.3 | 24.1 | 30.0 | — | — | — |
性能指標
| 項目 | 指標 | |
| 密度，Kg/m3 | 1350~1460 | |
| 維卡軟化溫度，℃ | ≥80 | |
| 縱向回縮率，% | ≤5 | |
| 二氯甲烷浸漬試驗，15℃，15min | 表面變化不劣于4N | |
| 落錘沖擊試驗（0℃）TIR，% | ≤5 | |
| 液壓試驗 | dn<40mm 20℃ 36MPa 1h | 無破裂，無滲漏 |
| dn≥40mm 20℃ 36MPa 1h | ||
| 20℃ 30MPa 100h | ||
| 60℃ 10MPa 1000h | ||
| 系統適用性試驗 | 連接密封性試驗 | 無破裂，無滲漏 |
| 負壓試驗 | 無破裂，無滲漏 | |
| 偏角試驗 | 無破裂，無滲漏 | |
|  | ||
 |
| ||
|  |
CNAS實驗室 三重檢測 |
國家級實驗室中心，所有產品都將嚴格執行原料、在線、成品三重檢驗，細致檢測，層層把關，質量更有保障。
|
| ||||